The SPX022AR.3 High Energy Fused Silica Lens is an AR.3 coated (at 355 nm), 1 inch (25.4 mm) diameter, HPFS 7978 plano-convex lens with an effective focal length of 100.0 mm at 546.1 nm. It is designed for high frequency laser pulses where standard grade fused silica does not perform very well. The special grade fused silica Corning HPFS 7978 has very low hydroxyl molecule presence compared to standard fused silica material, which results in less absorption of laser light and greatly reducing the chances of internal damage.

• 透镜形状

  Plano-Convex

• 直径

  25.4 mm

• 透镜材料

  HPFS 7978

• 增透膜

  355 nm

• 有效焦距

  100 mm  

• 表面质量

  15-5 scratch-dig

• 表面精度，不规则性

  λ/8

• 表面精度（光圈）

  1.5 λ  

• 表面平面度

  λ/10

• 后焦距

  96.71 mm  

• F/＃

  3.9  

• 曲率半径

  45.900 mm  

• 倒角

  0–0.8 mm face width

• 倒角公差

  45° ±15°, typical

• 直径公差

  +0/-0.1 mm

• 焦距公差

  ±1 %

• 中心厚度

  4.792 mm  

• 中心厚度公差

  ±0.1 mm

• 通光孔径

  ≥central 90% of diameter

• 镀膜代码

  AR.3

• 清洁

  See How to Clean Optics

• 损伤阈值

  15 J/cm2, 20 nsec pulses, 10 Hz at 1064 nm

• 反射率

  Ravg<0.25% @ 355 nm

SPX022AR。3高能熔融二氧化硅透镜为AR.3涂层(355 nm)，直径1英寸(25.4 mm)，有效焦距为100.0 mm，有效焦距546.1 nm的HPFS 7978平凸透镜。适用于标准等级熔融石英性能不佳的高频激光脉冲。与标准熔融二氧化硅材料相比，特种熔融二氧化硅Corning HPFS 7978具有非常低的羟基分子存在，导致激光吸收更少，大大降低了内部损伤的机会。